Production

• ESP stages of common version
  • Flow rate range is from 15 up to 470 m³ per day
  • Material: powder infiltered steel ЖГ р1Д15-пр
  • Material of friction pair: alloying infiltered steel with antifriction admixtures.
  • Density – 7,6 – 7.8 g/cm³
  • Strength limit 300 МПа
  • Hardness 70-100HRB
  
  
• ESP stages of corrosion-resistant version
  • Flow rate range is from 15 up to 470 m³ per day
  • Material: powder infiltered stainless steel Х11Н8М1, 5Д20-пр
  • Material of friction pair: corrosion-resistant infiltered steel with antifriction admixtures.
  • Density – 7,4 – 7.8 g/cm³
  • Strength limit 300 МПа
  • Hardness 70-90HRB
  
  
• Constructive parts from powder stainless steels
  • The parts are manufactured from powder stainless steels of austenite, ferrit and austenite-ferrite types with density range from 6.4 up to 7.8 g/cm³ per day.
  • Parts are intended for operating in corrosion-active environments and may be used as non-magnetic motor parts.
  
  
• Antifriction and constructive iron-based parts.
• Radial and axial plain bearings.
  • Bearings with surface from wear-resistant tungsten carbide- based material are used as a friction pair, operating in heavy abrasive-containing environment and as intermediate bearings of wear-resistant submersible equipment.
  • Bearing surface material possess high abrasive wear resistance as well as high plastic properties, it is insensible to load impact and vibration.
  • Bearings may be produced from corrosion-resistant material for operating in severe environments.